点击图片查看原图材质单
COMPONENT 成分
RESULT 结果
1.
Ash content, not more % 灰分，不超过%
0.14
2.
Mass fraction of sulphur, not more % 硫的质量分数，不超过%
Low sulphur residual oil
低硫残油
0.5
3.
Temperature of the flash, not less oC火花温度，不低于℃
in the closed crucible闭口坩埚
65
In the open crucible oC开口坩埚，℃
110 min最低
4.
The temperature of solidification, not higher oC凝固温度，不高于℃
25
5.
Kinematics viscosity运动粘度
118 max最高
6.
Water content含水量
0.5%
7.
Mechanical impurities机械杂质
Lower than低于 0.1%
8.
Acidity酸度
Lower than低于 5 mg KOH/ 100ml
9.
Alkalinity含碱量
Nil
10.
Gross Calorific Value总热值 Kcal/kg / KJ/kg
Min最低9200/41300
11.
Density at 15.0 deg. C Kg/l在15℃时的密度kg/l
0.8900-0.9200
12.
Hydrogen Sulfide Content (H2S) pom硫化氢含量（硫化氢）聚甲醛
0.5 max最高
13.
Carbon Residual残碳
Lower than低于 7%
14.
Vanadium钒 (V) ppm
23
15.
Aluminium 铝(Al) ppm
5
16.
Silikon硅 (Si) ppm
12
17.
Nickel 镍(Ni) ppm
49
18.
Asphaltenes 沥青质m/m
3.6%
19.
Destilation @4 mm Hg Extracted to 760 mm Hg蒸馏@4毫米汞柱，提取到760毫米汞柱
Initial Boiling Point deg. C
初沸点℃
216
5% recovered deg. C
恢复5%，℃
259
10% recovered deg. C
恢复10%，℃
310
20% recovered deg. C
恢复20%，℃
358
30% recovered deg. C
恢复30%，℃
445
40% recovered deg. C
恢复40%，℃
502
50% recovered deg. C
恢复50%，℃
534
60% recovered deg. C
恢复60%，℃
538
75% recovered deg. C
恢复75%，℃
545
80% recovered deg. C
恢复80%，℃
90% recovered deg. C
恢复90%，℃
20
Final Boiling point deg. C 最终沸点
550
21
Percent Recovered vol 回收体积
78%
22
Residue vol 残留提及
22%
23
COMPONENT 成分
RESULT
24
Total Nitrogen m/m 总氮
0.19%
25
20. Sodium (Na) ppm 钠
15